Significant Quantum Efficiency Enhancement of InGaN Red Micro-Light-Emitting Diodes with a Peak External Quantum Efficiency of up to 6%

Citations Over TimeTop 10% of 2023 papers

Abstract

We demonstrate a significant quantum efficiency enhancement of InGaN red micro-light-emitting diodes (μLEDs). The peak external quantum efficiency (EQE) of the packaged 80 × 80 μm2 InGaN red μLEDs was largely increased to 6.0% at 12 A/cm2, representing the significant process in exploring the efficiency of InGaN red μLEDs. The improvement of the EQE is attributed to the significant enhancement of the quantum efficiency, which is confirmed by the electron–hole wavefunction overlap in the InGaN quantum well from the band gap simulation and the photoluminescence intensity ratio at room temperature/low temperature. Ultrasmall 5 × 5 μm2 InGaN red μLEDs were also obtained, which show a high peak EQE of 4.5%. This work demonstrates a simple approach to achieving highly efficient InGaN red μLEDs, which are very promising candidates for ultrasmall red μLEDs required by AR/VR displays.

Related Papers

• → La2MgTiO6:Bi3+/Mn4+ photoluminescence materials: Molten salt preparation, Bi3+ → Mn4+ energy transfer and thermostability(2020)21 cited
• → Photoluminescence of porous Si, oxidized then deoxidized chemically(1992)109 cited
• → Study of delocalized and localized states in ZnSeO layers with photoluminescence, micro-photoluminescence, and time-resolved photoluminescence(2019)7 cited
• → Excitons imaging in hybrid organic-inorganic films(2012)3 cited
• → Ballistic effect and new concept of Si wire photoluminescence(2003)1 cited